Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina

Publication ,  Journal Article
Morrison, AD; Stormont, RW; Cocks, FH
Published in: J. Am. Ceram. Soc. (USA)
1975

High Na vapor pressure, peritectic decomposition, and high reactivity of the melt complicate the growth of β-alumina crystals. These difficulties were overcome by using a high-pressure (300 psig) growth chamber, Na2O-rich melts, and Ir for all surfaces in contact with the melt. These procedures were combined with the edge-defined film-fed growth technique to produce single-crystal β-alumina tubes and ribbons

Duke Scholars

Published In

J. Am. Ceram. Soc. (USA)

Publication Date

1975

Volume

58

Issue

1

Start / End Page

41 / 43
 

Citation

APA
Chicago
ICMJE
MLA
NLM
Morrison, A. D., Stormont, R. W., & Cocks, F. H. (1975). Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina. J. Am. Ceram. Soc. (USA), 58(1), 41–43.
Morrison, A. D., R. W. Stormont, and F. H. Cocks. “Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina.” J. Am. Ceram. Soc. (USA) 58, no. 1 (1975): 41–43.
Morrison AD, Stormont RW, Cocks FH. Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina. J Am Ceram Soc (USA). 1975;58(1):41–3.
Morrison, A. D., et al. “Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina.” J. Am. Ceram. Soc. (USA), vol. 58, no. 1, 1975, pp. 41–43.
Morrison AD, Stormont RW, Cocks FH. Edge-defined film-fed growth of β-alumina and Mg-substituted β-alumina. J Am Ceram Soc (USA). 1975;58(1):41–43.

Published In

J. Am. Ceram. Soc. (USA)

Publication Date

1975

Volume

58

Issue

1

Start / End Page

41 / 43