Disordering in 69GaAs/71GaAs isotope superlattice structures

Publication ,  Journal Article
Tan, TY; You, HM; Yu, S; Gosele, UM; Jager, W; Boeringer, DW; Zypman, F; Tsu, R; Lee, ST
Published in: J. Appl. Phys. (USA)
1992

Undoped 69GaAs/71GaAs isotope superlattice structures grown by molecular beam epitaxy on n-type GaAs substrates, doped by Si to ~3×1018 cm-3, have been used to study Ga self-diffusion in GaAs by disordering reactions. In the temperature range of 850-960 °C, the secondary ion mass spectrometry (SIMS) measured Ga self-diffusivity values showed an activation enthalpy of 4 eV, and are larger than previously compiled Ga self-diffusivity and Al-Ga interdiffusivity values obtained under thermal equilibrium and intrinsic conditions, which are characterized by a 6 eV activation enthalpy. Characterizations by SIMS, capacitance-voltage (C-V), and transmission electron microscopy showed that the as-grown superlattice layers were intrinsic which turned into p type with hole concentrations of ~2×1017 cm-3 after annealing, because the layers contain carbon. Dislocations of a density of ~106-107 cm-2 were also present. However, the factor responsible for the presently observed larger Ga self-diffusivity values appears to be Si out-diffusion from the substrate, which was determined using C-V measurements. Out-diffusion of Si decreases the electron concentration in the substrate which causes the release of Ga vacancies into the superlattice layers where they become supersaturated. This Ga vacancy supersaturation leads to enhanced Ga self-diffusion in the superlattice layers

Duke Scholars

Published In

J. Appl. Phys. (USA)

DOI

Publication Date

1992

Volume

72

Issue

11

Start / End Page

5206 / 5212

Related Subject Headings

  • Applied Physics
  • 51 Physical sciences
  • 49 Mathematical sciences
  • 40 Engineering
  • 09 Engineering
  • 02 Physical Sciences
  • 01 Mathematical Sciences
 

Citation

APA
Chicago
ICMJE
MLA
NLM
Tan, T. Y., You, H. M., Yu, S., Gosele, U. M., Jager, W., Boeringer, D. W., … Lee, S. T. (1992). Disordering in 69GaAs/71GaAs isotope superlattice structures. J. Appl. Phys. (USA), 72(11), 5206–5212. https://doi.org/10.1063/1.352002
Tan, T. Y., H. M. You, S. Yu, U. M. Gosele, W. Jager, D. W. Boeringer, F. Zypman, R. Tsu, and S. T. Lee. “Disordering in 69GaAs/71GaAs isotope superlattice structures.” J. Appl. Phys. (USA) 72, no. 11 (1992): 5206–12. https://doi.org/10.1063/1.352002.
Tan TY, You HM, Yu S, Gosele UM, Jager W, Boeringer DW, et al. Disordering in 69GaAs/71GaAs isotope superlattice structures. J Appl Phys (USA). 1992;72(11):5206–12.
Tan, T. Y., et al. “Disordering in 69GaAs/71GaAs isotope superlattice structures.” J. Appl. Phys. (USA), vol. 72, no. 11, 1992, pp. 5206–12. Manual, doi:10.1063/1.352002.
Tan TY, You HM, Yu S, Gosele UM, Jager W, Boeringer DW, Zypman F, Tsu R, Lee ST. Disordering in 69GaAs/71GaAs isotope superlattice structures. J Appl Phys (USA). 1992;72(11):5206–5212.

Published In

J. Appl. Phys. (USA)

DOI

Publication Date

1992

Volume

72

Issue

11

Start / End Page

5206 / 5212

Related Subject Headings

  • Applied Physics
  • 51 Physical sciences
  • 49 Mathematical sciences
  • 40 Engineering
  • 09 Engineering
  • 02 Physical Sciences
  • 01 Mathematical Sciences